PENGARUH WAKTU SOLUTION TREATMENT DAN AGING TERHADAP KEKERASAN DAN KEKUATAN TARIK ALUMINIUM PADUAN AA 7075 – T6

Authors

  • Amira Naafila Brawijaya University
  • Anindito Purnowidodo Brawijaya University
  • Putu Hadi Setyarini Brawijaya University

DOI:

https://doi.org/10.21776/jrm.v15i1.862

Keywords:

Aluminium, Solution Treatment, Aging, Micro Structure, EDS, Hardness

Abstract

Aluminium 7075 is a material used to plane body, because this material is corrosion-resistant, and its properties can be formed well, low density and light. Aluminium 7075-T6 which is mainly used for aircraft manufacturing, has a content of 0,37% Zn, 0,13% Mg, 0,07% Cu and 0,20% Si. Because this material 7075-T6 is heat treatable. It will be treated with the solution treatment (420ºC) and aging treatment (250ºC) each in 1hour and 2,5 hours to make precipitation. The hight strength and low hardness to find out the characteristics of aluminium 7075-T6 tensile strength testing, hardness testing and EDS (Energy Dispersive X-Ray Spectroscopy) testing will be carried out. And the result of tensile strength testing for raw material has an ultimate tensile strength (125,000MPa), elongation (0,02%) and the result of Rockwell hardness testing has (10,36 HRt). This material done by processed solution treatment with temperature (420ºC/hour, 2,5 hours/ 150ºC) has an ultimate tensile strength (95,833 MPa), elongation (0,26%) and for the Rockwell hardness testing the result is (49,2 HRt). The heat treatment made the solution treated aluminium grain bigger but increasing the strength because of precipitation.

Author Biography

Amira Naafila, Brawijaya University

Mechanical Engineering, Material Manufacture

References

A. B. Hadzley, A. A. Anis, M. N. Farizan, M. H. Osman, T. Norfauzi, and S. Noorazizi, “Analysis of surface integrity and formation of material side flow in dry and wet machining of aluminum alloy,” J. Adv. Manuf. Technol., vol. 12, no. Specialissue1, pp. 501–512, 2018.

D. P. Putri, B. J. Siswanto, D. Antonius, J. T. Mesin, and U. K. Indonesia, “Pengaruh Waktu Artificial Aging terhadap Struktur Kristal Kerapatan Dislokasi dan Kekerasan pada Paduan Al-7075 Effect of Artificial Aging Time on Crystal Structure, Dislocation Density And Hardness of Al-7075 Alloy,” vol. 4, no. 2, pp. 114–128, 2020.

N. Dariyanto, H. Hartopo, MT, “Stuktur Pada Nose Bay Side Plate Plate Pesawat T-34C-1 Charlie” INDEPT, Vol. 4, No. 3, 2014

R. B. S. Majanasastra, “Pengaruh Variable Waktu (Aging Heat Treatment ) Terhadap Peningkatan Kekerasan Permukaan Dan Struktur Mikro,” vol. 3, no. 2, pp. 87–101, 2015.

I. Saefuloh, A. Pramono, W. Jamaludin, and I. Rosyadi, “Studi Karakterisasi Sifat Mekanik Dan struktur Mikro Material Piston Alumunium-Silikon Alloy,” FLYWHEEL, J. Tek. mesin Untirta, vol. IV, no. 2, pp. 56–63, 2018.

W. H. Candra and Sutarsis, “Pengaruh Temperatur dan Waktu Tahan Aging Presipitasi Hardening terhadap Struktur Mikro,” J. Tek. Pomits, vol. 3, no. 2, pp. 232–236, 2014.

R. M. D. dan Sutarsis, “Pengaruh Temperatur Aging dan Waktu 5Al-1 % Y untuk Aplikasi Komponen Otomotif,” vol. 3, no. 2, 2014.

R. M. D. dan Sutarsis, “Pengaruh Temperatur Aging dan Waktu 5Al-1 % Y untuk Aplikasi Komponen Otomotif,” vol. 3, no. 2, 2014.

B. Budiarto, D. Antonius, and B. A. Putra, “Analisis Pengaruh Waktu Artificial Age Terhadap Kekerasan, Densitas Dan Struktur Kristal Paduan Alumunium (7075) Untuk Bahan Sirip Roket,” J. Kaji. Ilm., vol. 20, no. 1, pp. 13–28, 2020.

S. Syahputra, “Pengaruh Penambahan Cu Dan Solution Treatment Terhadap Sifat Mekanis Dan Struktur Mikro Pada Aluminium Paduan a356,” no. 14, pp. 39–45, 2

H. M. Unggul, H. Ardhyananta, and A. T. Wibisono, “Analisis Pengaruh Komposisi Aluminium (Al) Terhadap Struktur Mikro, Kekerasan dan Laju Korosi Anoda Tumbal Berbasis Seng (Zn) untuk Kapal dengan Metode Pengecoran,” J. Tek. ITS, vol. 7, no. 2, 2019.

Y. Xu, L. Zhan, S. Li, and X. Wu, “Effect of Stress-Aging Treatments on Precipitates of Pre-retrogressed Al-Zn-Mg-Cu Alloy,” Xiyou Jinshu Cailiao Yu Gongcheng/Rare Met. Mater. Eng., vol. 46, no. 2, pp. 355–362, 2017.

Downloads

Published

2024-05-15

Issue

Section

Articles