Analisis Variasi Arus Pengelasan Kombinasi SMAW-FCAW dengan Kampuh Double V-Groove terhadap Kekerasan dan Struktur Mikro Dissimilar Material JIS G3101-SS400 dan ASTM A36
DOI:
https://doi.org/10.21776/ub.jrm.2021.012.02.19Keywords:
Current, FCAW, Hardness, Microstructure, Welding, SMAWAbstract
This study aims to determine the effect of variations of the current with combining two welding techniques SMAW and FCAW in double v-groove against the hardness and microstructure of the dissimilar material of JIS G3101-SS400 and ASTM A36. JIS G3101 SS400 and ASTM A36 each with a thickness of 10 mm were used as the materials. The combination of SMAW welding with E7018 electrodes and FCAW with E71T-1 were used as the welding techniques. The current used in SMAW welding were 60 A, 75 A, and 90 A. While in FCAW welding the current used were 190 A, 205 A, and 220 A. Hardness and microstructure tests were carried out on each sample. The results of the study showed that the current in welding process affect the hardness value and microstructure of material. The higher the welding current, the value of hardness of the material going to decrease and vice versa. The highest hardness values in SMAW and FCAW welding are at currents of 60 A and 190 A. Then the current in the welding process also affect the microstructure produced in the weld and HAZ. The formed microstructure containing pearlite and ferrite. The higher welding current, the percentage of pearlite produced increase and the percentage of ferrite decrease.
References
HADI, EKO SASMITO., “Analisa Pengelasan Mild Steel (ST.42) Dengan Proses SMAW, FCAW, dan SAW Ditinjau Dari Segi Kekuatan dan Nilai Ekonomisâ€, Jurnal Ilmu Pengetahuan dan Teknologi Kelautan, v. 6, n. 2, pp. 107-117, Mar. 2012.
JULIAN, NANDA., et al., “Analisa Perbandingan Kekuatan Tarik Pada Sambungan Las Baja SS400 Pengelasan MAG Dengan Variasi Arus Pengelasan dan Media Pendingin Sebagai Material Lambung Kapalâ€, Jurnal Teknik Perkapalan, v.7, n.4, pp. 277-285, Okt. 2019.
HERMANTO, DEDDY; ARY SUBAGIA, I D.G, BUDIARSA, I NYOMAN., “Kekuatan Tarik Dan Kekerasan Sambungan Las Baja ST 37 Dengan Menggunakan Variasi Elektrodaâ€,Teknik Desain Mekanika, [S.l.], v. 6, n. 1, pp. 47-52, Sep. 2017.
WIRYOSUMARTO, H., DAN OKUMURA, T.,Teknologi Pengelasan Logam, Jakarta, Pradnya Paramita, 2000.
SONAWAN, H., SURATMAN R., Pengantar untuk Memahami Proses Pengelasan Logam, 2 ed., Bandung, CV Alfabeta, 2006.
BINTARTO, REDI., et al., “Analisa Struktur Mikro dan Kekuatan Bending Sambungan Las TIG dengan Perbedaan Kuat Arus Listrik pada Logam Tak Sejenis Aluminium Paduan 5052-Baja Galvanis dengan Filler Al-Si 4043â€, Jurnal Rekayasa Mesin, [S.l.], v. 11, n. 1, pp. 125-131, May 2020.
AWS.,Welding Handbook, 9 ed, v. 2., Miami: American Welding Society, 2020.
SYAHRANI, A., NAHARUDDIN., MUHAMMAD, N., “Analisis Kekuatan Tarik, Kekerasan, dan Struktur Mikro Pada Pengelasan SMAW Stainless Steel 312 Dengan Variasi Arus Listrikâ€, Jurnal Mekanikal, v. 9, n.1, pp. 814-822, Jan. 2018.
KHIYAARUL., NABIELAH, A., et al., “Analisis Pengaruh Variasi Flow Rate Gas Pelindung Pada Pengelasan FCAW-G Terhadap Struktur Mikro dan Kekuatan Mekanik Sambungan Material Grade Aâ€, Jurnal Teknik ITS, v. 7, n. 2, pp. 186-191, 2018.
RIDWAY,B., KADIR,A., DEDI, S., “Analisis Pengaruh Arus Pengelasan Pada Sudut Elektroda 70â° Terhadap Sifat Kekerasan dan Struktur Mikro Baja Karbon Rendah Menggunakan JIG Weldingâ€, Jurnal Ilmiah Mahasiswa Teknik Mesin, v.2, n.2, pp.50-55, Nov. 2016.
ASIBELUO,I.S., EMIFONIYE,E., “Effect of Arc Welding Current on the Mechanical Properties of A36 Carbon Steel Weld Jointsâ€, SSRG International Journal of Mechanical Engineering, v.2, n.9, pp. 32-4, Sep. 2015.
WIBOWO, H., ILMAN, M., ISWANTO, T., PRIYO., “Analisa Heat Input Pengelasan terhadap Distorsi, Struktur Mikro dan Kekuatan Mekanis Baja A36â€, Rekayasa Mesin , [S.l.], v. 7, n. 1, p. pp. 5-12, May 2016.
ABSON, D.J., PARGETER, R.J., “Factors Including Strength Microstructure And Toughness Of As Deposited Manual Metal Arc Welds Suitable For C-Mn Steel Fabricationsâ€, International Metal Reviews, v.31, n.4, pp. 141-196, 1986.
ASKAR, S., et al., “Pengaruh Preheat dan Tempering Terhadap Kekerasan dan Sturuktur Mikro Hasil Pengelasan Baja JIS SS 400â€, Dinamika Teknik Mesin, v. 3, n.1, pp.16-25, Jan. 2013.
HERMAWAN, M., et al., “Pengaruh Arus Terhadap Struktur Mikro dan Sifat Mekanik Produk Las Tembaga dan Baja Karbon Dengan Metode Tungsten Intert Gas (TIG)â€, Jurusan Teknik Mesin Fakultas Teknik Universitas Muhammadiyah Surakarta, pp. 1-14, Jan. 2016.
Downloads
Published
Issue
Section
License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.