Pengaruh Thermal Shock dan Komposisi Grafit, Kaolin (Clay) terhadap Struktur Makro dan Ketahanan Impact Kowi Berbahan Dasar Limbah Evaporation Boats

Sinta Indiarti Nurrohmah, Rusiyanto Rusiyanto, Rahmat Doni Widodo, Wirawan Sumbodo

Abstract


The purpose of this study was to determine the effect of thermal shock and composition of graphite, kaolin (clay) on the macrostructure and impact resistance of crucible based on the waste of evaporation boats. The variation applied was composition waste of evaporation boats, graphite and kaolin 50%:25%:25%; 40%:30%:30%; 70%:15%:15%. Then the thermal shock standard temperature variation is ∆T = 100°C - 500°C. Specimens formed according to the ASTM D256 size (63.5x12.7x12.7) mm with compaction load 80 kg/cm2. Continuing the sintering process at a temperature of 1150°C holding time of 2 hours. Tests include XRD test for the waste of evaporation boats, thermal shock test, impact test and macro photo. The results showed that the highest average impact resistance is 0.01772659 Joule/mm2 with the composition of 50%: 25%: 25% without thermal shock. The lowest average resistance impact is 0.00637474 Joule/mm2 with the composition of 70%: 15%: 15% and 500°C thermal shock temperature. Based on the data, the higher treatment of temperature in thermal shock makes the lower impact resistance of the specimen.


Keywords


Thermal Shock; Waste of Evaporation Boats; Graphite; Kaolin; Crucible

Full Text:

PDF

References


AMSTEAD, B. H., OSTWALD P. F dan BEGEMAN M. L., Teknologi Mekanik 2, Erlangga,1986.

BARSOUM, M., M.W. BARSOUM, Fundamental of Ceramics, CRC Press, 2002.

HAMZAH, M SADAT, “Karakterisasi Kaolin Kab Barru Sebagai Bahan Dasar Keramik”,Jurnal Mek-trik, v. 6, n. 19, pp. 120-125, 2005.

LU T. J., AND N. A., FLECKTHE, “Thermal Shock Resistance of Solids”, v.46, n.13, pp. 4755-4768, 1998.

LUKMAN, A.D., RUSIYANTO dan RAHMAT D.W., “Pengaruh Thermal Shock dan Komposisi Arang Sekam Padi, Grafit terhadap Sifat Fisis dan Mekanis Kowi Berbahan Dasar Clay (Lempung)”, Jurnal Teknik Mesin, 2017.

MUDZAKIR, H., SUNYOTO, RAHMAT D.W., et al., “Pengaruh Variasi Fraksi Alumina (Al2O3), Magnesium Oxide (MgO) dan Clay dari Genteng Mentah terhadap Kekuatan Impact dan Struktur Mikro Refractory Pada Tungku Listrik”, Jurnal Teknik Mesin, 2018.

MUHHIBUDIN, Pengujian Dan Validasi Alat Uji Impact Type Charpy (Impact Testing Machine), Universitas Teuku Umar Alue Peunyareng, Meulaboh, 2005.

RAMASAMY, RAMAMMOORTHY, DAVID M RUSINKO, GREGORY A. STROKESATER dan JAMES A. RICHKER, Gains in Metalizing Economic through Improved Evaporator Boat Design, GE Advanced - Material Ceramics, 2006.

SINURAYA, ANDIKA SURANTA, Pelapisan Cr-Al dan Boron Nitrida sebagai Dopping Baja Karbon Rendah dengan Metode Ball Milling, Universitas Sumatera Utara, Medan, 2018.

SUPARJO dan PURNOMO, “Variasi Temperatur Pemanasan Pada Proses Perlakuan Panas terhadap Kekerasan dengan Material SS-304L”, v.16, n.2, pp. 170-178, 2012.

SURDIA,T., SAITO, Pengetahuan Bahan Teknik, Jakarta, Pradnya Paramitha, 1986.

WARDHANA, GALANG WISNU dan ARDHYANANTA HOSTA, “Pengaruh Penambahan Grafit Terhadap Sifat Tarik, Stabilitas Thermal dan Konduktivitas Listrik Komposit Vinil Ester/Grafit Sebagai Pelat Bipolar Membran Penukar Proton Sel Bahan Bakar (PEMFC)” v.3, n. 1, pp. F-7 - F-12, 2014.

WIDAYANA, GEDE., NYOMAN PASEK NUGRAHA dan NYOMAN ARYA WIGRAHA, “Pengaruh Variasi Temperatur Sintering Terhadp Umur Tanur Pada Industri Kerajinan Gong di Gianyar”, v.03, n.02, pp. 439-449,2014.

WIDODO, RAHMAT DONI dan RUSIYANTO, “Pengaruh Komposisi Kaolin terhadap Densitas dan Kekuatan Bending pada Komposit Fly-Ash Kaolin”, v. 9, n. 1, pp. 45-50, 2011.

United Nations Environment Progamme, www.energyefficiencyasia.org, Diakses: Mei 2019.




DOI: https://doi.org/10.21776/ub.jrm.2020.011.02.15

Refbacks



Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.