Pengaruh Fraksi Volume Dan Panjang Serat Pelepah Lontar (Borassus Flabellifer) Terhadap Kekuatan Tarik Dan Kekuatan Impak Komposit Bermatrik Epoksi

Amros Alfonsius Tuati, Anindito Purnowidodo, Achmad As’ad Sonief

Abstract


This study was conducted using epoxy resin as ligature and midrib lontar fibers (borassus flabellifer) as brace. Composite was made by varied fiber volume fraction 10%, 30% and 50% with length variation 10 mm, 20 mm, and 30 mm. The composite production used hand lay-up method. The test result showed the highest composite tensile strength about 31.607 Mpa in volume fraction 10% with fiber length 30 mm. The lowest composite tensile strength was about 16.855 Mpa in fiber volume fraction 10% and 20 mm in fiber length. Moreover, the highest composite impact strength was 0.00163 J/mm in fiber volume fraction 50% with fiber length 30 mm and the lowest impact strength was 0.00214 J/mm 2 in fiber volume fraction 10% and 10 mm fiber length. The kind of composite fracture tended to have brittle fracture with mechanism of fiber pull out.


Keywords


Midrib Lontar Fibers; Volume Fraction; Fiber Length; Epoxy Composite Impact Strength

Full Text:

PDF


DOI: https://doi.org/10.21776/ub.jrm.2015.006.01.5

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.