PENGARUH TEMPERATUR AUSTEMPERING TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO BESI COR KELABU DENGAN NIKEL 10% UNTUK KOMPONEN BOILER PLTU

Authors

  • Fikri Widyansyah Universitas Sultan Ageng Tirtayasa
  • Efendi Mabruri Badan Riset dan Inovasi Nasional (BRIN)
  • Alfirano Alfirano Universitas Sultan Ageng Tirtayasa

DOI:

https://doi.org/10.21776/jrm.v14i3.1650

Keywords:

Gray Cast Iron, Nickel, Austempering, Eutectic Cell

Abstract

Effect of austempering temperature on microstructure and mechanical properties gray cast iron with 10%wt nickel for boiler combustion application has been studied. Cast iron with the JIS FCD 45 standard with a minimum tensile strength of 414 MPa and a hardness of 187 HB is commonly used for this application. To improve its mechanical properties such as strength and hardness, austempering heat treatment usually applied. Austempering was carried out at 250°C, 300°C, 350°C, 400°C, and 450°C for 1 hour, with the same austenization temperature of 850°C for 1 hour. The highest increase in hardness was found at the austempering temperature of 250°C. The hardness was 321.80 HB or 19.30% of the initial hardness of 259.70 HB. In terms of strength, the highest increase occurred at the austempering temperature of 250°C which was 257 MPa or 31.52% of the initial strength of 176 MPa.

References

ESDM. Konsumsi Listrik Per Kapita Indonesia Capai 1.109 kWH/kapita pada Triwulan IV 2021. 2021. [Online]. Available at: < https://gatrik.esdm.go.id/ > [Diakses pada tanggal 29 Juli 2023].

Roswati, N. Jasmid, E., Eza, B., Perancangan Boiler dengan Memanfaatkan Sampah Kering untuk Bahan Bakar Pltu Mini 3 Kw Stt-PLN. JURNAL POWERPLANT, v. 5, n. 1, pp. 1-10, 2017.

Pribadi, A. T., Hardi, W. & Abbas, M. F. Analisis Kerusakan Bearing dan Shaft Chain Grate Ditinjau dari Kenaikan Temperatur Pelumas terhadap Spesifikasi Menggunakan ANSYS FLUENT 2019 R3. Dinamika Jurnal Teknik Mesin Unkhair, v. 5, n. 2, pp. 30-34, 2020.

Green, A. S., & Waite, M. L. The redesign of chain grate stoker links to reduce pollutant emissions: aerodynamic design. Fuel, v. 83, n. 10, pp. 1391-1395, 2004.

Saputra, S., S. Pranoto, Y. R. Aldori, S. Ali, Junaidi, A. Herlambang, M. Yusuf R. S., M. Idris. Analisis Pengaruh Panas dan Beban terhadap Kerusakan Traveling Grate pada Boiler Di PLTU Tembilahan 2×7 MW. JOURNAL OF MECHANICAL ENGINEERING, MANUFACTURES, MATERIALS AND ENERGY, v. 7, n. 2, pp. 113-127, 2023.

Zhou, S., Shen, Y., Zhang, H., & Chen, D. Heat treatment effect on microstructure, hardness and wear resistance of Cr26 white cast iron. Chinese Journal of Mechanical Engineering, v. 28, n. 1, pp. 140-147, 2015.

Niazi, N., Nisar, S., & Shah, A. Austempering heat treatment of AISI 4340 steel and comparative analysis of various physical properties at different parameters. International Journal of Multidisciplinary Sciences and Engineering, v. 5, n. 10, pp. 6-11, 2014.

Banerjee, M. K. Fundamentals of Heat Treatment Metals and Alloys. In Comprehensive Materials Finishing, v. 2, pp. 1-49, 2016.

Ankamma, K. Effect of trace elements on the properties of grey cast iron. Materials Technology, v. 19, n. 3, pp. 153–154, 2016.

Vadiraj, A., Balachandran, G., & Kamaraj, M. Effect of misch metal inoculation on microstructure, mechanical and wear properties of hypoeutectic gray cast irons. Materials & Design, v. 30, n. 10, pp. 4488–4492, 2009.

Tewary, U., Paul, D., Mehtani H. K., S. Bhagavath, Alankar A., G. Mohapatra, S. S. Sahay, Ajay S. Pawar, S. Karagadde, I. Samajdar. The origin of graphite morphology in cast iron. Acta Materialia, v. 226, 117660, 2022.

Colin-García, E., A. C. Ramirez, G. Reyes-Castellanos, J. A. Rommero-Serano. Influence of nickel addition and casting modulus on the properties of hypo-eutectic ductile cast iron. Journal of Mining and Metallurgy, Section B: Metallurgy, v. 55, n. 2, pp. 283-293, 2019.

Benam, A. S. Effect of alloying elements on austempered ductile iron (ADI) properties and its process: Review. China Overseas Foundry, v.12, n. 1, pp. 54-70, 2015.

Rajan, T. S., Sharma, C. P., & Sharma, A. K. Heat treatment: principles and techniques. PHI Learning Pvt. Ltd., 2011.

Wang, B., Han, X., Barber, G. C., & Pan, Y. Wear Behavior of Austempered and Quenched and Tempered Gray Cast Irons under Similar Hardness. Metals, v. 9, n. 12, 1329, 2019.

Bayati, H., & Elliott, R. Austempering process in high manganese alloyed ductile cast iron. Materials science and technology, v. 11, n. 2, pp. 118-129, 1995.

Sckudlarek, W., Krmasha, M. N., Al-Rubaie, K. S., Preti, O., Milan, J. C., & da Costa, C. E. Effect of austempering temperature on microstructure and mechanical properties of ductile cast iron modified by niobium. Journal of Materials Research and Technology, v. 12, pp. 2414-2425, 2021.

Rashidi, M. M., & Idris, M. H. The effects of solidification on the microstructure and mechanical properties of modified ductile Ni-resist iron with a high manganese content. Materials Science and Engineering: A, v. 597, pp. 395-407, 2014.

Downloads

Published

2023-12-15

How to Cite

Widyansyah, F., Mabruri, E., & Alfirano, A. (2023). PENGARUH TEMPERATUR AUSTEMPERING TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO BESI COR KELABU DENGAN NIKEL 10% UNTUK KOMPONEN BOILER PLTU. Jurnal Rekayasa Mesin, 14(3), 1023–1031. https://doi.org/10.21776/jrm.v14i3.1650

Issue

Section

Articles