ANALISIS PENGARUH VARIASI ARAH PENGELASAN HARDFACING TERHADAP KEKUATAN TARIK DAN STRUKTUR MIKRO PADA BAJA ASTM A36

Authors

  • Jatmoko Awali Institut Teknologi Kalimantan
  • M. Arzil Maulana Institut Teknologi Kalimantan
  • Fikan Mubarok Rohimsyah Institut Teknologi Kalimantan
  • Yunita Triana Institut Teknologi Kalimantan

DOI:

https://doi.org/10.21776/jrm.v15i1.1507

Keywords:

Hardfacing, Welding Direction, Tensile Strength, ASTM A36, SMAW

Abstract

Welding is a metal joining process with filler or without filler. The welding method is also used to thicken the surface of the material or hardfacing. Hardfacing is a welding process with the aim of improving mechanical properties and is used on worn components by using SMAW welding, SMAW welding is used because it is relatively inexpensive and flexible. The purpose of this study was to determine the effect of hardfacing with SMAW welding direction variations on the tensile strength and microstructure of ASTM A36 steel material. The welding directions are horizontal, vertical and diagonal. This study used ASTM A 36 steel with a thickness of 5 mm. The welding electrode was E7018 with a diameter of 3.2 mm and a current of 130 A. After conducting this research, the highest average tensile strength value was found in the vertical direction, which was 474.74 N/mm2. The average value of the tensile strength in the diagonal direction is 446.715 N/mm2. The average horizontal tensile strength value is 420.785 N/mm2.

References

Ijomah, W.L., Childe, S.J., “A model of the operations concerned in remanufacture”. International Journal of Production Research, Vol. 45, No. 24, pp. 5857–5880, 2007.

Saini, S., Sahni, S., Singh, S., “A Review of Hardfacing and Wear Reducing Tech- niques onIndustrial Valves”. International Journal of Research In Engineering & TecShnol- ogy volume 4,23.

Waqas, A., Qin, X., Xiong, J., Wang, H., & Zheng, C., “Optimization of process parameters to improve the effective area of deposition in GMAW based additive manufacturing and its mechanical and microstructural analysis”. Metals, Washington: API.

Choteborsky, R, “Abrasive wear of high chromium fe-Cr-C hardfacing alloy”, research in agricultural Engineering. 2008.

Suryo Darmo, Braam Delfian Prihadianto “The Effect Of Hard Facing Process On The Hardness And Microstructure Of Bucket Tooth For Different Manganese Content” Jurnal Rekayasa Mesin, v. 13, n. 3, pp. 827 – 836, 2022.

Pradeep, A., Gk Balaji, S Muthukumaran, S Senthilkumaran., “ Optimization of friction welding of tube-to-tube plate using an external tool with filler plate”. Journal of materials engineering and performance 21, 1199-1204. 2012.

Soleh, A,A., Purwanto, H.,& Syafa’at, I., “Analisa Pengaruh Kuat Arus Terhadap Struktur Mikro, Kekerasan, Kekuatan Tarik, Pada Baja Karbon Rendah Dengan Las SMAW Menggunakan Jenis Elektroda E7016” , Cendekia Eksata, 2017.

Bintarto, Redi., et al., “Analisa Struktur Mikro dan Kekuatan Bending Sambungan Las TIG dengan Perbedaan Kuat Arus Listrik pada Logam Tak Sejenis Aluminium Paduan 5052-Baja Galvanis dengan Filler Al-Si 4043”, Jurnal Rekayasa Mesin, v. 11, n. 1, pp. 125-131, May 2020.

AWS D1.1., “Structural Welding Code Steel. American Welding Society”,2015.

ASME IX., “Qualifications Standard Forb Welding and Brazing Procedures, Welder, Braz- ers, and Welding and Brazing Operators”. The American Society of Mechanical Engineers. New York, 2010.

Ye Eun Jeong, Gwang Yong Shin, Do Sik Shim., “Effect of P21 buffer layer on interfacial bonding characteristics of high-carbon tool steel hardfaced through directed ener- gy deposition”, Department of Ocean Advanced Materials Convergence Engineering, Korea Maritime and Ocean University, 727 Taejong-ro, Yeongdo-Gu, Busan 49112, Republic of Korea. 2021.

Heri Wibowo, M.Noer Ilman , PriyoTri Iswanto “Analisa Heat Input Pengelasan terhadap Distorsi, Struktur Mikro dan Kekuatan Mekanis Baja A36’ Jurnal Rekayasa Mesin Vol.7, No.1 Tahun 2016: 5-12, Teknik Mesin dan Industri, Universitas Gadjah Mada, Jl. Grafika no 2 Yogyakarta 55281.

Ayan, Y. Dan Kahraman, N.,“Wire Arc Additive Manufacturing of LowCarbon Mild Steel Using Two Different 3D Printers”, Physics of Metals and Metallography, Vol. 122 No. 14, hal. 1521–1529.

Callister, William, D J., “Materials Science and Engineering an Introduction” John Wiley and Sons. Singapore. 2014

Zamil Moch Farid, Proses Pengelasan Listrik. Diambil dari. http://las listrik.blogspot.com. Terakhir diakses pada November 2014.

Downloads

Published

2024-05-15

Issue

Section

Articles