ANALISIS PENERAPAN COATING PADA BAJA ASTM A36 DENGAN VARIASI CAT TERHADAP LAJU KOROSI, KEKUATAN ADHESI DAN KETAHANAN IMPACT COATING
DOI:
https://doi.org/10.21776/jrm.v15i3.1500Keywords:
ASTM A36, Coating, Corrosion Rate, Adhesion StrengthAbstract
Corrosion is the most common damage experienced by steel structures due to the interaction between a metal and a corrosive environment. One way to prevent corrosion of steel is coating. A good coating must have a low corrosion rate, high adhesion, and material resistance to impact. This study aimed to compare the corrosion rate, adhesion strength, and impact coating values of the different types of paint between epoxy, alkyd, and polyurethane on A36 steel. The type of steel used in this study is ASTM A36 steel. In this study, the type of coating paint used varied. The types of coatings used are epoxy, alkyd, and polyurethane. Aluminum oxide with a mesh size of 24 is used as an abrasive material. Testing the corrosion rate using the electrochemical method, the test used to determine the adhesive power value using the pull off test method, and to determine the coating resistance value using the impact test method. This type of polyurethane coating has the most optimal value between epoxy and alkyd with a corrosion rate value of 9.09×10-5mmpy, an adhesion value of 15.06 MPa, and an impact coating resistance of 4.70 Joules. Based on the results obtained in this study, the different types of coatings affect the value of corrosion rate, adhesion, and impact.
References
J. A. Sukma and M. Yusuf Umardani, ST, “Pengerasan Permukaan Baja Karbon St 40 Dengan Metode Nitridasi Dalam Larutan Kalium Nitrat,” Rotasi, vol. 13, no. 4, pp. 10–35, 2012.
H. U. Sajid and R. Kiran, “Influence of corrosion and surface roughness on wettability of ASTM A36 steels,” J. Constr. Steel Res., vol. 144, pp. 310–326, 2018, doi: 10.1016/j.jcsr.2018.01.023.
C. Trijatmiko et al., “213202-Analisa-Pengaruh-Material-Abrasif-Pada-B,” vol. 5, no. 2, pp. 231–235, 2016.
A. Struktur et al., “Pengaruh Variasi Konsentrasi Inhibitor Dari Kitosan Sisik Ikan Terhadap Perilaku Korosi Besi Astm A36: Studi Ekstrapolarisasi Tafel Dan EIS,” J. Rekayasa Mesin, no. December 2019, pp. 125–131, 2020.
V. Puspasari, P. A. Paristiawan, S. Herbirowo, and B. Adjiantoro, “Morphology and Microstructure Properties of Nanozeolite Coating on Iron Foam With Variation of Calcination Temperature and Chitosan,” J. Rekayasa Mesin, vol. 12, no. 3, pp. 561–571, 2021, doi: 10.21776/ub.jrm.2021.012.03.6.
J. V Koleske, Paint and Coating Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook. University of Virginia, 1995. doi: 10.1520/mnl17_14th-eb.
Y. K. Afandi, I. S. Arief, J. Teknik, S. Perkapalan, and F. T. Kelautan, “Jurnal Korosi (Abdi),” vol. 4, no. 1, pp. 1–5, 2015.
H. Pratikno and W. L. Dhanistha, “Material Abrasif Dan Ketebalan Polyurethane Coating Pada Baja Astm a36 Terhadap Analysis of the Effect of Abrasive Material and Polyurethane Coating Thickness Variations on Astm a36 Steel Towards Adhesion Strength and Faculty of Marine Technology,” 2020.
C. Debrilia, “Analisa Pengaruh Variasi Metode Coating pada pelat Baja ASTM A36 terhadap Prediksi Laju Korosi, Kekuatan Adhesi, dan Ketahanan Impact,” Pap. Knowl. . Towar. a Media Hist. Doc., 2014.
T. Mulyanto, Supriyono, and S. Parama Arta, “Pengaruh Perlakuan Awal Terhadap Daya Rekat Dan Kekuatan Lapisan Pada Proses Pengecatan Serbuk,” J. ASIIMETRIK J. Ilm. Rekayasa Inov., vol. 2, no. 1, pp. 25–32, 2020, doi: 10.35814/asiimetrik.v2i1.1186.
Christiam Bernal Murillo, “ASTM D4541-95 Pull-Off Adhesion Test Standard,” vol. 06.02. pp. 1–12, 1995.
ASTM, “D2794 Standard test method for resistance of organic coatings to the effects of rapid deformation (impact),” Astm D2794, vol. 93, no. Reapproved, pp. 1–3, 1993, doi: 10.1520/D2794-93R10.2.
P. R. Roberge, 59. Corrosion Engineering Principles and Practice, McGraw-Hill, New York, US. 2008.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Untung Budiarto, Parlindungan Manik, Ghiyats Abiyyu Kusuma

This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.