PENGARUH VARIASI SUDUT DAN JARAK PENEMBAKAN SANDBLASTING PADA PROSES PRETREATMENT TERHADAP KUALITAS PELAPISAN CAT DAN SIFAT KOROSI PADA BAJA KARBON RENDAH
DOI:
https://doi.org/10.21776/jrm.v15i1.1382Keywords:
Carbon Steel, Sandblasting, Surface Roughness, Open Circuit Potential (OCP)Abstract
The purpose of this study was to determine the effect of variations in the angle and distance of sandblasting on paint coating quality and corrosion properties of low carbon steel. The success of a coating is highly dependent on surface roughness, so sandblasting is needed to clean and create a surface roughness profile with the aim that the paint can coat the surface perfectly. The test method used in this research is the pull off test method for testing the adhesive strength of paint and open circuit potential (OCP) for testing the corrosion potential. The sandblasting variations used are angles of 45⁰, 60⁰, 75⁰ and nozzle distances of 15 cm, 35 and 50 cm. The tests carried out were roughness, paint thickness, paint adhesive strength and corrosion potential. From the test results it can be concluded that the greater the angle and the closer the sandblasting nozzle distance, the greater the surface roughness. The greater surface roughness affects the paint layer to be thicker and has a high paint adhesion strength, resulting in a smaller corrosion potential. In this study, the highest test results were obtained at an angle of 75⁰ and a distance of 15 cm with a surface roughness value of 5.981 µm, a paint thickness of 115 µm, a paint adhesive strength of 7.28 MPa and an initial corrosion potential position of -0.101 V then a final position of -0.063 V.
References
Kementerian perindustrian, “Pengembangan Industri Perkapalan Dapat Prioritas,” kemenperin.go.id, 2020. https://kemenperin.go.id/artikel/21493/Pengembangan-Industri-Perkapalan-Dapat-Prioritas (accessed Sep. 06, 2022).
Fahmi Ali, “Pemerintah Pacu Pertumbuhan Industri Komponen Perkapalan,” tempo.co, 2017. https://bisnis.tempo.co/read/847399/pemerintah-pacu-pertumbuhan-industri-komponen-perkapalan (accessed Sep. 06, 2022).
A. Hendrawan, “Analisa tingkat kebisingan kamar mesin pada kapal,” in Wijayakusuma Prosiding Seminar Nasional: Jaringan Penelitian (Jarlit) Cilacap “Menuju Cilacap 4.C (Creativity, Critical Thingking, Communication And Colaboration), 2020, pp. 10–15. [Online]. Available: https://ejournal.unugha.ac.id/index.php/jarlit/article/view/260/206
Y. K. Afandi, I. S. Arief, and A. Amiadji, “Analisa laju korosi pada pelat baja karbon dengan variasi ketebalan coating,” J. Tek. ITS, vol. 4, no. 1, pp. 1–5, 2015, doi: 10.12962/j23373539.v4i1.8931.
P. Zhang, G. Meng, Y. Wang, B. Lei, and F. Wang, “Significantly enhanced corrosion resistance of Ni–Cu coating modified by minor cerium,” Corros. Commun., vol. 2, pp. 72–81, 2021, doi: 10.1016/j.corcom.2021.07.002.
Y. C. Surbakti, “Analisa Laju Korosi pada Pipa Baja Karbon dan Pipa Galvanis dengan Metode kehilangan berat,” Institut Teknologi SepuluhNopember, 2017.
C. Nurhidayat, “Pengaruh variasi sudut dan jarak penembakan terhadap kekasaran permukaan dan kekuatan rekat cat pada proses sandblasting,” Universitas Brawijaya, 2018. [Online]. Available: http://repository.ub.ac.id/id/eprint/9760
E. Sulistyo and P. H. Setyarini, “Pengaruh waktu dan sudut penyemprotan pada proses sand blasting terhadap laju korosi hasil pengecatan baja AISI 430,” J. Rekayasa Mesin, vol. 2, no. 3, pp. 205–208, 2011, [Online]. Available: https://rekayasamesin.ub.ac.id/index.php/rm/article/view/131
A. Rudawska, I. Danczak, M. Müller, and P. Valasek, “The effect of sandblasting on surface properties for adhesion,” Int. J. Adhes. Adhes., vol. 70, pp. 176–190, 2016, doi: 10.1016/j.ijadhadh.2016.06.010.
S. J. Sisworo, “Studi Komparasi Proses Abrasive Blasting Pada Pembangunan Kapal Dikaji Dari Segi Teknis Dan Ekonomis,” undip, 2009. http://eprints.undip.ac.id/5490/ (accessed Jan. 26, 2021).
J. Krawczyk, M. Bembenek, Ł. Frocisz, T. ´Sleboda, and M. Pa´cko, “The effect of sandblasting on properties and structures of the DC03/1.0347, DC04/1.0338, DC05/1.0312, and DD14/1.0389 steels for deep drawing,” Materials (Basel)., vol. 14, no. 3540, pp. 1–18, 2021, doi: https://doi.org/10.3390/ma14133540.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Indra Adi Saputra, Teguh Dwi Widodo, Lilis Yuliati
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.