KARAKTERISASI LAPISAN OKSIDA HASIL ANODIZING PADA ALUMINIUM DENGAN VARIABEL WAKTU PENCELUPAN

Authors

  • Andika Wisnujati Universitas Muhammadiyah Yogyakarta
  • Ferriawan Yudhanto Universitas Muhammadiyah Yogyakarta

DOI:

https://doi.org/10.21776/jrm.v14i2.1309

Keywords:

Anodizing, Aluminum, Immersion Time, Oxide Layer

Abstract

Anodizing is an electrolytic coating process that converts aluminum into aluminum oxide. The anodizing process is widely used in the manufacturing industry, especially in automotive components. Its utilization has benefits such as resistance to scratches, ease of maintenance, and added decorative value. The purpose of this study was to determine the effect of time variations on the hardness and thickness of the oxide layer in the 6xxx series of aluminum anodizing processes. The variation of time used in the immersion process is 20, 30, and 40 minutes, with an electric current of 2 amps and a voltage of 24 volts. After that, the dyeing and sealing process is carried out. The tests carried out included testing of hardness (Vickers) and the thickness of the oxide layer (coating thickness gauge). The results of the highest hardness test of 112.9 VHN were obtained at a time variation of 40 minutes, with an average layer thickness of 5.07 m. It can be said that the amount of time spent in the anodizing process has an effect on how hard the oxide layer gets and how thick it is on the 6xxx series of aluminum metal.  

References

G. E. Totten and D. S. Mackenzie, Handbook of Aluminum: Volume 2: Alloy production and materials manufacturing. CRC press, 2003.

A. Wisnujati, M. Yusuf, and A. Hudiatma, "Karakterisasi Pengecoran Poros Berulir (Screw) dengan Variabel Paduan Unsur Titanium Boron Dan Magnesium," Jurnal Rekayasa Mesin, vol. 13, no. 1, pp. 29-36, 2022.

R. Raharjo, T. D. Widodo, and R. Bintarto, "Desain Manufaktur Bracket Aluminium," Jurnal Rekayasa Mesin, vol. 9, no. 2, pp. 119-125, 2018.

P. Puspitasari, D. Puspitasari, M. I. N. Sasongko, Andoko, And H. Suryanto, "Tensile strength differences and type of fracture in artificial aging process of duralium against cooling media variation," in AIP Conference Proceedings, 2016, vol. 1778, no. 1: AIP Publishing LLC, p. 030012.

H.-C. Chen, A. Wisnujati, A. M. Widodo, and C.-W. Lung, "Grey Relational Analysis and Grey Prediction Model (1, 6) Approach for Analyzing the Electrode Distance and Mechanical Properties of Tandem MIG Welding Distortion," Materials, vol. 16, no. 4, p. 1390, 2023.

K.-H. Lee, S.-Y. Yang, and J.-G. Yang, "Optimization of heat-treatment parameters in hardening of titanium alloy Ti-6Al-4V by using the Taguchi method," The International Journal of Advanced Manufacturing Technology, vol. 90, no. 1, pp. 753-761, 2017.

M. I. Kido, S. Sugiarto, and D. B. Darmadi, "Perubahan Sifat Mekanik Hasil Pengelasan Gesek Aluminium 6061 Akibat Perubahan Temperatur Lingkungan," Jurnal Rekayasa Mesin, vol. 12, no. 1, pp. 95-102, 2021.

M. Muzaki, I. Mashudi, M. Fakhruddin, A. M. Anwar, R. A. N. Paranata, and G. Wiganata, "Analisis Pengaruh Variasi Beda Potensial dan Waktu Proses Anodizing terhadap Karakteristik Lapisan Oksida Aluminium 6061," Jurnal Rekayasa Mesin, vol. 17, no. 1, pp. 59-66, 2022.

R. A. Himarosa et al., "Simultaneous Double-Sided Metal Inert Gas Welding of AA5052 Aluminum Alloy T-Joints," in Materials Science Forum, 2022, vol. 1067: Trans Tech Publ, pp. 53-59.

D. I. Tsamroh, A. Suprapto, and P. E. Setyawan, "Optimasi Parameter Anodizing pada Aluminium 6061 dengan Metode Taguchi," 2020.

J. Zhang et al., "Anodization of aluminum in a sealed container," Electrochemistry Communications, vol. 129, p. 107086, 2021.

V. Fiore, F. Di Franco, R. Miranda, M. Santamaria, D. Badagliacco, and A. Valenza, "Effects of anodizing surface treatment on the mechanical strength of aluminum alloy 5083 to fibre reinforced composites adhesive joints," International Journal of Adhesion and Adhesives, vol. 108, p. 102868, 2021.

E. Budiyanto and L. D. Yuono, "Peranan aerasi sel elektrolisis dalam pembentukan pori pada proses anodizing logam aluminium," Turbo: Jurnal Program Studi Teknik Mesin, vol. 7, no. 2, 2018.

B. W. Sidharta, "Pengaruh Konsentrasi Elektrolit dan Waktu Anodisasi Terhadap Ketahanan Aus, Kekerasan Serta Ketebalan Lapisan Oksida Paduan Aluminium Pada Material Piston," Jurnal teknologi technoscientia, pp. 010-021, 2014.

R. Nurendra and R. H. Rahmanto, "Analisis Pengaruh Kuat Arus Listrik dan Waktu Proses Anodizing pada Outer Tube Front Fork Model XY Terhadap Ketebalan Lapisan," Jurnal Ilmiah Teknik Mesin, vol. 6, no. 1, pp. 36-40, 2018.

A. Widodo and M. N. Ilman, "Pengaruh Frekuensi Getaran Terhadap Sifat Fisis Dan Mekanik Pada Sambungan Las Mig Aluminium Paduan AA 6061-T6," Jurnal Rekayasa Mesin, vol. 13, no. 1, pp. 171-178, 2022.

M. Fatkhurouf, N. Mulyaningsih, and C. Pramono, "Pengaruh Ekstrak Kulit Manggis Terhadap Pewarnaan Aluminium Hasil Anodizing," Jurnal Teknik Mesin MERC (Mechanical Engineering Research Collection), vol. 2, no. 1, 2019.

X. Salahudin, H. Setiawan, and K. Suharno, "Pengaruh Variasi Kuat Arus Listrik Pada Proses Anodizing Terhadap Kekerasan dan Struktur Mikro Permukaan Aluminium," Journal of Mechanical Engineering, vol. 3, no. 2, pp. 1-6, 2020.

F. Nugroho, "Pengaruh rapat arus anodizing terhadap nilai kekerasan pada plat aluminium paduan aa seri 2024-t3," Angkasa: Jurnal Ilmiah Bidang Teknologi, vol. 7, no. 2, pp. 39-48, 2015.

D. Aditia, R. Usman, and Y. Yuniati, "Pengaruh Variasi Arus Dan Waktu Pada Anodisasi Type Hard Proses Terhadap Kekerasan Permukaan Aluminium," Jurnal Mesin Sains Terapan, vol. 3, no. 2, pp. 47-52, 2019.

E. E. Febriyanti, "Optimasi Proses Pelapisan Anodisasi Keras pada Paduan Aluminium," Metalurgi, vol. 26, no. 2, pp. 109-116, 2015.

A. Pramono, A. A. Alhamidi, and R. N. Fadila, "Pengaruh Parameter Terkontrol Pada Proses Accumulative Roll Bonding (Arb) Terhadap Sifat Mekanik dan Mikrostruktur Aluminium Seri 6 (AA6061)," Flywheel: Jurnal Teknik Mesin Untirta, vol. 2, no. 1, pp. 68-73, 2018.

D. Masruri, "Pengaruh Larutan Asam Sulfat Pada Proses Anodisasi Terhadap Kekerasan Permukaan Aluminium," in Seminar Nasional Rekayasa Teknologi Manufaktur, 2021, vol. 1, pp. 7-10.

Anonim. "Anodizing Aluminium." IQS Directory. https://www.iqsdirectory.com/ articles/aluminum-anodizing/anodized-aluminum.html (accessed January 22, 2023).

P. Rachmawati and A. Wisnujati, "Pengaruh Penambahan 2, 5% Ti-B Terhadap Sifat Mekanik Poros Berulir (Screw) Berbahan Dasar 40% Aluminium Bekas dan 60% Piston Bekas," Jurnal Engine: Energi, Manufaktur, dan Material, vol. 1, no. 2, pp. 8-18, 2017.

V. Sekatskii, O. Gavrilova, N. Merzlikina, Y. A. Pikalov, Y. Y. Pikalov, and I. Kaposhko, "Two-Point Calibration Of Coating Thickness Gauges: What Needs To Be Considered To Improve Measurement Accuracy," in IOP Conference Series: Materials Science and Engineering, 2019, vol. 537, no. 3: IOP Publishing, p. 032068.

Downloads

Published

2023-08-15

How to Cite

Wisnujati, A., & Yudhanto, F. (2023). KARAKTERISASI LAPISAN OKSIDA HASIL ANODIZING PADA ALUMINIUM DENGAN VARIABEL WAKTU PENCELUPAN . Jurnal Rekayasa Mesin, 14(2), 525–536. https://doi.org/10.21776/jrm.v14i2.1309

Issue

Section

Articles