Variasi Ukuran terhadap Kekerasan dan Laju Keausan Komposit Epoxy Alumunium-Serbuk Tempurung Kelapa untuk Kampas Rem

Ario Kristian Taka, FX. Kristianta, Imam Sholahuddin

Abstract


The aim of this research was to investigate the influence of the particle size of coconut shell powder on hardness and wear rate om aluminium epoxy based composite. Experimental method was used in this study by using four configurations of particle size. The configuration includes comersial powder and particle size of 300 µm, 425 µ and 600 µm. The results showed that the highest and smallest hardness value obtained by 300 µm of 63.67 kg/mm2 and 600 µm is 41.67 kg, respectively. However, the highest and smallest wear rate obtained by 600 µm is 8,70 x 10-6 gram/s.mm2 and 300 µm is 1,17 x 10-6 gram/s.mm2, respectively. This phenomena occured due to the coconut shell powder size of 300 µm is well and uniformly spread.

Keywords


brake shoes; composite; epoxy; coconut shell; aluminium

Full Text:

PDF

References


Wahyudi, Didik, dkk. 2002. Optimasi Kekerasan Kampas Rem dengan Metode Desain Eksperimen. Surabaya: Universitas Kristen Petra.

D. Kiswiranti, Sugianto, N. Hindarto, Sutikno. 2009. Pemanfaatan Serbuk Tempurung Kelapa Sebagai Alternatif Serat Penguat Bahan Friksi Non-Asbes Pada Kampas Rem Sepeda Motor. Semarang: Universitas Negeri Semarang (Unnes).

Santoso, dkk. 2013. Studi Pemanfaatan Campuran Serbuk Tempurung Kelapa-Aluminium Sebagai Material Alternatif Kampas Rem Sepeda Motor Non- Asbestos. Surakarta: UNS.

Syahid, Muhammad, dkk. 2011. Analisa Sifat Mekanik Polimer Matriks Komposit Berpenguat Fly Ash Batubara Sebagai Kampas Rem. Makasar: Universitas Hasanuddin.

Siswanto, Beni. 2008. Analisa Perbandingan Disk Brake Produk Asli Terhadap Disk Brake Imitasi Pada Motor GL Pro. Jakarta: Universitas Mercu Buana.

Priyambodo, Bambang Hari, dan Palmiyanto, Martinus Heru. 2014. Pengaruh Variasi Komposisi Bahan Komposit Limbah Kulit Mete/Phenolic Dengan Penguat Skrap Alumunium Terhadap Sifat Fisik dan Mekanik Sebagai Bahan Alternative Kampas Rem Non As-bestos. Surakarta: Akademi Teknologi Warga Surakarta.

Mubarrok, Muh Husni. 2014. Pengaruh Ujuran Serbuk Kuningan Terhadap Ketahanan Aus, Koefisien Gesek, dan Kekerasan Kampas Rem. Surakarta: Universitas Muhhammadiyah Surakarta.

Imam, Pramuko I.P, Dkk 2009. Pengaruh Komposisi Serat Kelapa Terhadap Kekerasan, Keausan Dan Koefisien Gesek Bahan Kopling Gesek Kendaraan. Surakarta: Universitas Muhammadiyah.

Irfan, Pramuko, 2009, Pengaruh Variasi Tekanan Kompaksi Terhadap Ketahanan Kampas Rem Gesek Sepatu. Surakarta: Universitas Muhammadiyah Surakarta.




DOI: http://dx.doi.org/10.21776/ub.jrm.2017.008.03.5

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.